Abstract
In this paper, low temperature oxygen plasma treatment method was adopted to process the carbon fiber surface. Flexural Strength test method was utilized to represent f composite material flexural strength. This paper observed flexural failure morphology of composite material by aid of SEM, then it compared the mechanical property, hygroscopicitiy and flexural strength retention rate of composite material before and after the plasma treatment. Results showed that the optimum treatment conditions of carbon fiber were 300W treatment power and 15-minute treatment time. Under the condition, the highest flexural strength value be increased by 19.55%.Saturated bibulous is low and bibulous rate is slow, flexural strength retention rate is 94.9%. And at the same time PES-C resin matrix can be strengthened, which will further improve the mechanical properties of composite materials.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.