Abstract
The effect of oxygen on stability of isothermal omega precipitates in Ti-29Nb-13Ta-4.6Zr was examined using X-ray powder diffraction, transmission electron microscopy, and atom probe tomography. Two alloys with 0.1 and 0.4 mass% oxygen were subjected to single step, and two-step annealing heat-treatments to respectively promote omega and alpha formation. After second step annealing, large volume fraction of omega precipitates was retained in 0.4 mass% O alloy while mainly alpha phase was observed in TNTZ-0.1O. The enhanced stability of omega in the higher oxygen containing TNTZ alloys questions the conventionally accepted understanding that oxygen destabilizes the omega phase in titanium alloys.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.