Abstract
Films of composites (Co45Fe45Zr10)x(Al2O3)100–x, (Co84Nb14Ta2)x(SiO2)100–x, (Co41Fe39B20)x(SiO2)100–x and multilayer heterogeneous composite–composite structures {[(Co45Fe45Zr10)x(Al2O3)100–x]/[(Co45Fe45Zr10)x(Al2O3)100–x + N2]}n, {[(Co45Fe45Zr10)x(Al2O3)100–x]/[(Co45Fe45Zr10)x(Al2O3)100–x + O2]}n, {[(Co41Fe39B20)x(SiO2)100–x]/[(Co41Fe39B20)x(SiO2)100–x + O2]}n, and {[(Co84Nb14Ta2)x(SiO2)100–x]/[(Co84Nb14Ta2)x(SiO2)100–x + O2]}n have been deposited using the ionbeam sputtering method with a cyclic supply of reaction gases during deposition. The structure and magnetic properties of the films have been studied. It has been shown that the introduction of an oxidized interlayer makes it possible to suppress the perpendicular magnetic anisotropy in the (Co45Fe45Zr10)x(Al2O3)100–x composite with the metallic phase concentration higher than the percolation threshold.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.