Abstract
The present paper deals with the influence of non-metallic inclusions on fatigue life in the high cycle fatigue and the very high cycle fatigue regime. For that purpose, several castings of steel 42CrMo4 (AISI 4140, DIN EN 1.7225) were produced by using recently developed novel metal-melt filters. The specimens were tested in hot-isostatically pressed and heat treated condition. After fatigue failure every fracture surface was intensively investigated by scanning electron microscopy in order to define the type, the size, the chemical composition, the morphology and the location of the crack initiating discontinuity. Subsequently, Murakami’s √area model was used for the evaluation of the influence of non-metallic inclusions on the fatigue life. In the present investigation four common types of chemical compositions of crack initiating discontinuities were identified. Furthermore, four different internal failure types and their influence on the fatigue life in cast steel were investigated and described. Thus, the present contribution proposes a basic correlation determined from fatigue lives in case of various internal crack initiation types. The key parameters for fatigue life prediction in case of internal fatigue failure in the very high cycle fatigue regime are (i) the size of the crack initiating discontinuity, (ii) the inclusion depth and (iii) the crack initiating failure type.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.