Influence of nitrogen overpressure on the nitridation, densification and formation of β-SiAlONs produced by silicothermal reduction

Abstract

Abstract β-SiAlON materials (with z = 1) with 2 mol% DyAG have been synthesised by silicothermal reduction under different nitrogen pressures. The possibility of rapidly nitriding silicon and forming the SiAlON phase has been investigated through its reaction sequence of formation under different pressures. β-SiAlONs were fully nitrided (degree of nitridation greater than 93%) and formed after a 1-h hold at 1400 °C, or after a straight ramp to 1500 °C under 0.7 MPa of nitrogen. This was not achievable under static nitrogen at atmospheric pressure where the degree of nitridation was only 43% and β-SiAlON phase represented only about 60% of the crystalline phase assemblage at the same temperature. The formation of β-SiAlON depended on the formation of Si 3 N 4 whose reaction rate was enhanced by nitrogen overpressures.