Abstract
AbstractThe influence of nanolimestone/nanoCaCo3 (NC) on the properties of ultrahigh-performance concrete (UHPC) cured at standard and heat conditions was experimentally investigated. The NC was used at ratios of 1, 2, and 3% as partial mass replacement for cement. Incorporating NC accelerated the hydration reactions of UHPC because of the nucleation effect. On the mechanical properties aspect, a threshold value of the NC content was found so that the compressive, flexural strengths, and flexural to compressive strength ratio of the UHPC were found to increase as the NC content increased towards the threshold content, and then to decrease with the increase of NC contents when the threshold was surpassed. Conversely, replacing cement with NC decreased flowability and increased the amount of autogenous shrinkage of the UHPC. While the NC accelerated the cement hydration process, it also acted as an effective filling material, resulting in enhanced mechanical properties and denser microstructure compared wit...
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.