Abstract
The economic impact of surface damage and component failure arising from solid particle impact in the UK has been estimated in 1997 at around £20 million [1]. The additional complexity associated with erosion in a corrosive environment such as that encountered in the chemical and hydro-carbon extraction industries can significantly accelerate surface wear and material loss. In this study, surface material response of a stainless 316 alloy subject to erosion and erosion–corrosion was investigated by focused ion beam (FIB) and transmission electron microscopy (TEM) techniques. Samples tested in a slurry pot apparatus using 1% uncrushed silica at 7m/s for 60min, both in water and 3.5% NaCl solution. Site specific FIB–TEM lamellas showed that solid particle impact resulted in extensive crater and lip formations and a martensitic phase transformation at the surface. The presence of a corrosive fluid resulted in preferential dissolution of the martensitic phase, reducing the work hardening behaviour and promoting greater elongation to failure and thus higher erosion–corrosion rates. These results are discussed in light of the extensive literature on solid particle impact and corrosion by considering the influence of nano-scale phase changes which can often only be observed using transmission electron microscopy.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.