Influence of microalloy type and content on induced precipitation kinetics in microalloyed steels

Abstract

Using torsion tests, and applying the back extrapolation method, the statically recrystallized fraction has been determined for low carbon microalloyed steels with different V, Nb and Ti contents, at different temperatures and an equivalent strain of 0.20%. At temperatures below the static recrystallization critical temperature (SRCT), or the temperature at which strain induced precipitation commences, recrystallized fraction against time curves show a plateau caused by precipitations. The formation of the plateau makes it possible to evaluate precipitation-time-temperature (PTT) diagrams, and thus to know the precipitation kinetics. The PTT diagrams show that an increase in the microalloy content raises SRCT and reduces incubation time. For similar Nb, V and Ti contents, Nb is the element which raises SRCT the most. Der statische Rekristallisierungsanteil mikrolegierter Stähle mit verschiedenen Gehalten an Vanadium, Niob und Titan wurde durch Torsionsversuche bei unterschiedlichen Temperaturen ermittelt. Hieraus lassen sich Rekristallisierungsanteil-Zeit-Kurven erstellen, die bei Temperaturen unterhalb der kritischen Rekristallisierungtemperatur (SRCT) ein Plateau zeigen. Das Auftreten dieser Zone mit konstantem Rekristallisierungsanteil ermöglicht es, Auscheidung-Zeit-Temperatur-(PTT)-Diagramme aufzustellen und die Auscheidungskinetik kennenzulernen. Die PTT-Diagramme zeigen, daß die SRCT mit steigendem Gehalt an Mikrolegierungselementen ansteigt und die Inkubationszeit abnimmt. Auf jeden Fall bewirkt Niob einen stärkeren Anstieg der SRCT als Vanadium oder Titan