The influence of Mg content on the microstructures and mechanical properties at room temperatures of Al–3.5Cu–(0.71–1.81)Mg alloys was studied. Precipitation phases in the alloys were identified by TEM and HRTEM. The results show that when Mg contents increase from 0.71 to 1.81 wt%, the precipitates are transformed from S, S″, Ω, and θ′ phases to S and S″ phases, and Ω phase is first observed in Al–3.48Cu–0.71 Mg alloy with Cu/Mg mass ratio of 5 during the conventional aging heat treatment (190 °C/12 h). Regard to aging hardness effect of the tested alloys, the hardness of the alloys improves with the increase of Mg content, but the increases become slow when Mg content is greater than 1.35 wt%.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.