Abstract
The influence of Mg content on the degree of sensitization (DoS) of Al-xMg-0.5Mn (wt%) alloys (where x varies from 3.36 wt% to 8.85 wt%) was investigated via the nitric acid mass loss test (NAMLT). NAMLT upon sensitized specimens revealed that mass loss was negligible below ~4.01 wt% Mg, while for Mg content ≥4.01 wt%, mass loss increased monotonically. The calculated equilibrium β-phase fractions were contrast with the DoS values. Additionally, the influence of the Mg content on corrosion was investigated via potentiodynamic polarization testing, in conjunction with microhardness measurements. We found that Mg additions lead to an increase in hardness without causing any significant impact on electrochemically determined corrosion current density; however, Mg content has a major impact on intergranular corrosion as determined from NAMLT.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.