Influence of metal co-deposition on silicon nanodot patterning dynamics during ion-beam sputtering

Abstract

We address the impact of metal co-deposition in the nanodot patterning dynamics of Si(100) surfaces under normal-incidence 1 keV Ar+ ion-beam sputtering (IBS). In particular, the effect of both the metal nature (Fe or Mo) and flux has been studied. Morphological and compositional evolution were followed by atomic force microscopy (AFM) and Rutherford backscattering spectrometry, respectively. For the same type of impurity, the dynamics is faster for a higher co-deposition flux, which also drives to larger asymptotic roughness and wavelength. Mo co-deposition yields rougher surfaces for a lower metal coverage than Fe and, remarkably, higher ordered patterns. X-ray photoelectron spectroscopy reveals the formation of silicide bonds even before pattern onset, stressing the relevant role of the affinity of the co-deposited metals for silicon. Further, current-sensing AFM performed at the initial and asymptotic stages indicates that the nanodot structures are metal-rich, resulting in coupled compositional and morphological patterns. These results are discussed in terms of phase segregation, morphology-driven local flux variations of impurities and silicide formation. This analysis reveals that the underlying (concurrent) mechanisms of pattern formation are complex since many processes can come into play with a different relative weight depending on the specific patterning conditions. From a practical point of view, it is shown that, by proper selection of the process parameters, IBS with metal co-deposition can be used to tune the dynamics and pattern properties and, interestingly, to produce highly ordered arrays.