Abstract
Solidification behavior of Al-Y and Al-Si were investigated for different melt temperatures. Levitation casting technique was used to achieve a cooling rate of around ∼2000K/s during the experiment. Light optical microscopy (LOM) and Scanning electron microscopy (SEM) were used to analyze the samples. An energy dispersive system (EDS) analysis of SEM was performed on the samples to identify the phases. Plate like structure of Al8Y3 primary phase was observed at low melt temperature with small percentage of peritectic transformation of Al8Y3 and liquid melt into Al9Y2. A pre-dentritic star like crystal of Al3Y was observed in a fine eutectic matrix at very high melt temperature. Amount and number of primary Si crystals formed in a unit area during the solidification increases as the melt temperature increases. It is believed the melt temperature affects the solidification pattern by changing chemical short range order.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.