Abstract
In the present research, nano hydroxyapatite (HA) powder doped with magnesia (MgO) was studied. The dopant was added to pure HA powder and ball milling was done for 1 hour. Green samples, in the form of discs and rectangular bars, were prepared and consolidated in air at temperatures ranging from 1000°C to 1300°C. The sintered samples were characterized to determine the phase stability, relative density, hardness, fracture toughness and Young’s modulus. The phase analysis revealed that the HA phase was not disrupted regardless of dopant additions and sintering temperature. It has been revealed that all HA samples achieved > 98% relative density when sintered between 1100oC–1300oC. However, the addition of 0.5 wt% MgO when sintered at 1100°C was found to be most beneficial in aiding sintering with samples exhibiting the highest Young’s modulus of 122.15 GPa and fracture toughness of 1.64 MPam1/2 as compared to 116.57 GPa and 1.18 MPam1/2 for the undoped HA.
Sign-in/Register to access full text options 
Free) 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call