Influence of long-term water storage on the physical and chemical properties of four different dental cements

Abstract

To evaluate and compare the physical and chemical properties of four different dental cements under long-term water storage. A glass-ionomer cement (A:Fuji I), a resin reinforced glass-ionomer (B: Fuji Plus), a self-adhesive resin cement (C:G-Cem), and an etch & rinse resin cement (D: Duolink) were taken as samples. According to ISO 4049, water sorption and solubility of four resin cements under different storage times (1 week, 1, 3, 6 and 12 months) were calculated (n = 5), meanwhile their surface Knoop micro hardness values were measured. Surface cracks were detected on sample B and C after 12 months. Sample A was fragmentized after 6 months. Sample B showed significantly lower surface hardness after 12 months than it did after the first 24 hours of water storage (P < 0.05). Sample D showed significantly lower water sorption than other cements did at all exam time point. The highest water sorption values were observed in Sample D after 1 month [(40.8±2.5) µg/mm(3)], in Sample B after 3 months [(551.3±22.5) µg/mm(3)], in Sample C after 12 months [(147.5±8.3) µg/mm(3)]. The highest solubility values were detected in Sample B after 3 months [(105.3±10.5) µg/mm(3)], in Sample C after 12 months [(79.3 ± 6.2) µg/mm(3)], and in Sample D after 12 months [(23.9 ± 6.9) µg/mm(3)]. Among the four types of cements, the etch & rinse resin cement showed the best stability of physical and chemical properties under long-term water storage.