Abstract
The influence of laser surface alloying (LSA) with Cr and Cr + Ni on the corrosion behaviour of type 304L stainless steel (SS) was investigated using potentiodynamic polarisation and electrochemical impedance spectroscopy (EIS) in chloride (0·5M NaCl) and acidic (1 N H2SO4) media. Surface alloying was carried out by laser cladding type 304L SS substrate with premixed powders of AISI type 316L SS and the desired alloying elements. The results indicated that Cr surface alloyed specimen exhibited a duplex (γ + α) microstructure with Cr content of ∼24 wt-%, whereas Cr + Ni surface alloyed specimen was associated with austenitic microstructure with Cr and Ni contents of ∼22 wt-% each. The potentiodynamic polarisation results in chloride solution indicated that LSA with Cr + Ni considerably enhanced the pitting corrosion resistance compared with LSA with Cr alone. In acidic media, such beneficial effects were not observed. Electrochemical impedance spectroscopy results showed an increase in semicircle arc for both chloride and acidic media for both Cr and Cr + Ni clad samples indicating improvement in the oxide film stability compared with untreated specimen. The polarisation resistance was higher and capacitance values of the laser clad specimen were lower than those in the untreated specimen. The microstructural changes and compositional variations produced by LSA are correlated to the corrosion behaviour.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.