Influence of laser power on microstructure and mechanical properties of fiber laser-tungsten inert gas hybrid welded Mg/Cu dissimilar joints

Abstract

Fiber laser-tungsten inert gas (TIG) hybrid welding technique has been developed for lap joining of dissimilar metals AZ31B Mg alloy to pure copper (T2). The influence of laser power on microstructure and mechanical properties of joints was investigated. The results indicated that acceptable joints could be obtained by adjusting the laser power to the range of 2000–3000 W. In particular, at the laser power of 2500 W the average tensile shear strength reached a maximum of 45.3 MPa, representing a 57% joint efficiency relative to the Mg sheet. Greater or less than 2500 W would cause over or under reaction at the interface, which resulted in the poor joint strength. The different morphologies including Mg–Cu eutectic structure, Mg–Cu intermetallic compound and Mg–Al–Cu ternary intermetallic compound were identified at the Mg/Cu interface. All the joints fractured at the Mg/Cu interface. However, the fracture mode was found to differ. For 2500 W the surface was characterized by tearing edge, while that with poor joint strength was almost dominated by smooth surface or flat tear pattern.