Abstract
The influence of irreversible hydrogen on the fatigue crack growth in cold-drawn high-strength steel was investigated to clarify the mechanism of fatigue strength degradation by irreversible hydrogen. The fatigue crack growth rate was accelerated by irreversible hydrogen in low ΔKeff region, and the acceleration increased with a decrease in ΔKeff. Moreover, the fatigue crack growth rate under irreversible hydrogen charged condition increased as the stress cycle frequency decreased. The behavior of irreversible hydrogen under cyclic loading was visualized using a hydrogen microprint technique. It was proved that irreversible hydrogen desorbed out from its trap site under cyclic loading.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.