Abstract
The effects of intermediate annealing (IA) on the microstructure and texture of Ni-9.3at%W substrates have been investigated by using electron backscattering diffraction and X-ray diffraction. Results suggest that IA can optimize the homogeneity of deformation microstructure. Higher IA temperatures (without undergoing recrystallization during IA) will increase the copper-type components of deformation texture and improve the content of cube texture after recrystallization. Sharp cube texture (97.2%) can be obtained at the optimum IA temperature of 650°C. The mechanism underlying the transition of deformation texture can be interpreted as that IA increases the dislocation slipping ability and suppresses the twinning deformation of Copper orientation in the subsequent rolling process. The observed strengthening of cube texture as a result of IA treatment is presumably attributed to the reduction of noncube nucleation and the optimization of preferential growth surrounding the cube nuclei.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: International Journal of Minerals, Metallurgy, and Materials
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.