Abstract
The aim of this article is to study the influence of interfacial structure development at interface on the fracture mechanism and the bond strength of cold roll bonded Al/Cu bimetal plate. The Al/Cu bimetal plates are produced by cold roll bonding and then sintered at different conditions. The bond strength of the Al/Cu bimetal plate increases generally to maximum values and then decreases to low values with increasing sintering temperature and time. Interfacial structures develop with increasing sintering temperature and time. The main interfacial layers are Al 2 Cu, AlCu, Al 3 Cu 4 and Al 4 Cu 9 . The formation and thickening of those intermetallic compounds promotes cracks propagation and weakens the bond strength of the bimetal plates. The fracture mechanism transforms from ductile to brittle cleavage with the development of interfacial structures. While the bond strength of the material starts to decrease, no obvious Kirkendall effect of void formation is observed in the present study.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.