Abstract
This article describes the influence of controlling in-flight hot particle characteristics on properties of plasma sprayed nanostructured yttria stabilized zirconia (YSZ) coatings. This article depicts dependence of adhesion strength of as-sprayed nanostructured YSZ coatings on particle temperature, velocity and size of the splat prior to impact on the metallic substrate. Particle temperature measurement is based on two-color pyrometry and particle velocities are measured from the length of the particle traces during known exposure times. The microstructure and adhesion strength of as-sprayed nano-YSZ coatings were studied. Field emission scanning electron microscopy results revealed that morphology of coating exhibits bimodal microstructure consisting of nano-zones reinforced in the matrix of fully melted particles. The coating adhesion strength is noticed to be greatly affected by the melting state of agglomerates. Maximum adhesion strength of 42.39 MPa has been experimentally found out by selecting optimum levels of particle temperature and velocity. The enhanced bond strength of nano-YSZ coating may be attributed to higher interfacial toughness due to cracks being interrupted by adherent nano-zones.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.