Abstract
The influence of hydrogen on a (Co0·2Cu0·2Mg0·2Ni0·2Zn0.2)O HEO with a rock salt structure was studied. Two forms of this HEO (nanopowder and sinter) were prepared via mechanochemical synthesis (MS) and additional heat treatment, respectively. The chemical stability of the synthesized samples in a pure hydrogen atmosphere was investigated using Sievert's technique. High-pressure hydrogenation at 250 °C had no noticeable effect on the HEO sinter. The sintered sample was chemically, structurally, and morphologically stable, as confirmed via the XRD, Raman spectroscopy, SEM, and XPS techniques. Thermogravimetric analysis (TGA) showed the sinter to be stable in an argon gas mixture with 5 vol% of hydrogen and over the temperature range of up to 400 °C.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.