Abstract
Linear low density polyethylene (PE-LLD) and cast polypropylene (PPcast) films were irradiated in a 60Co γ-source. The total irradiation dose varied from 0kGy (unirradiated samples) to 200kGy. Oxygen transport was investigated by a manometric method and the structural changes were studied by differential scanning calorimetry (DSC) and Fourier transform infrared spectroscopy (FTIR). Free radicals decay as a function of time was monitored by electron spin resonance (ESR) spectroscopy. The results show that the γ-irradiation reduces oxygen permeability coefficient in both films. The reduction was associated with an increase in crystallinity. DSC thermograms revealed a decrease in PPcast melting point with increasing irradiation dose, indicating higher degradation compared to PE-LLD. The observed peak in FTIR spectra for both samples at 1716cm−1 corresponds to the stretching of the carbonyl and carboxylic groups which arise from the reaction of oxygen with the free radicals produced in the polymer matrix as a result of irradiation.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.