Abstract
Alloy 22 (N06022) is the current candidate alloy used to fabricate the external wall of the high-level nuclear waste containers for the Yucca Mountain repository. It was of interest to study and compare the general and localized corrosion susceptibility of Alloy 22 in fluoride and chloride solutions at 90 °C. Standard electrochemical tests such as cyclic potentiodynamic polarization, amperometry, and electrochemical impedance spectroscopy were used. Studied variables included the solution pH and the alloy microstructure (thermal aging). Results show that Alloy 22 is highly resistant to general corrosion in all the solutions tested. Thermal aging is not detrimental and even seems to be slightly beneficial for general corrosion at the higher solution pHs. Pitting corrosion was never observed. Crevice corrosion was found only for high chloride-containing solutions after anodic polarization. The presence of fluoride ions together with chloride ions seems to increase the susceptibility of Alloy 22 to crevice corrosion compared to pure chloride solutions.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.