Influence of growth temperature on the pinning landscape of YBa2Cu3O7− δ films grown from Ba-deficient solutions

Abstract

Cuprate coated conductors are promising materials for the development of large-scale applications, having superior performance over other superconductors. Tailoring their vortex pinning landscape through nanostructure engineering is one of the major challenges to fulfill the specific application requirements. In this work, we have studied the influence of the growth temperature on the generation of intrinsic pinning defects in YBa2Cu3O7−δ films grown by chemical solution deposition using low Ba precursor solutions. We have analysed the critical current density as a function of the temperature, applied magnetic field magnitude and orientation, J c(T,H,θ), to elucidate the nature and strength of pinning sites and correlate the microstructure of the films with their superconducting performance. An efficient pinning landscape consisting of stacking faults and associated nanostrain is naturally induced by simply tuning the growth temperature without the need to add artificial pinning sites. Samples grown at an optimized temperature of 750 °C show very high self-field J c values correlated with an overdoped state and improved J c(T,H,θ) performances.