Abstract
Al-7 wt% Ni alloy was directionally solidified upwards with different growth rates, V (8.3–489.5 μm/s) at constant temperature gradient, G (4.2 K/mm) using a Bridgman-type growth apparatus. The dependence of the dendritic microstructures such as primary dendrite arm spacing (λ1) and secondary dendrite arm spacing (λ2) on the growth rate were determined using a linear regression analysis. The present experimental results were also compared with similar previous experimental results. Measurements of microhardness (HV) and electrical resistivity (ρ) of the directionally solidified samples were carried out. The dependence of the microhardness and electrical resistivity on the growth rate (V) was also analyzed. According to these results, it has been found that, for increasing values of V, the values of HV and ρ increase. However, the values of HV and ρ decrease with increasing values of λ1 and λ2.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.