Abstract
ABSTRACTA study of the improvement of the mechanical and thermal properties of nanocomposites prepared with polypropylene (PP) and different graphene samples [graphene oxide (GO), reduced GO (RGO), and commercial graphene (G)] is presented. X‐ray diffraction (XRD) and X‐ray photoelectron spectroscopy characterization were applied to the graphene samples. The nanocomposites were characterized by thermogravimetric analysis, XRD, differential scanning calorimetry, transmission electron microscopy (TEM), tensile, and impact resistance tests. PP/RGO nanocomposites showed significant improvement in mechanical and thermal properties. Sample PP/RGO‐0.75 resulted in an increment in Young's modulus (51%), tensile strength (24%), and elongation at break (15%). This is attributed to a good dispersion state, a higher crystallinity percentage, and a good interfacial adhesion between PP and RGO. Sample PP/RGO‐0.50 exhibited an increase of 197 °C in the temperature at which a loss in weight of 5% occurred, compared to that for pure PP. The height of stacked layers calculated by XRD measurements was similar to the value observed by TEM. © 2019 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2020, 137, 48258.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.