Abstract
The paper reports on effect of grain-growth inhibitors MgO, Y2O3 and MnCO3 as well as Ca modification on the microstructure, dielectric, ferroelectric and electrocaloric (EC) properties of Ba0.82Sr0.18Sn0.065Ti0.935O3 (BSSnT). Furthermore, the effects of the sintering time and temperature on the microstructure and the electrical properties of the most promising material system Ba0.62Ca0.20Sr0.18Sn0.065Ti0.935O3 (BCSSnT-20) are investigated. Additions of MgO (xMgO = 1%), Y2O3 (xY2O3 = 0.25%) and MnCO3 (xMnCO3 = 1%) significantly decreased the mean grain size of BSSnT to 0.4 µm, 0.8 µm and 0.4 µm, respectively. Ba0.62Ca0.20Sr0.18Sn0.065Ti0.935O3 (BCSSnT-20) gained a homogeneous fine-grained microstructure with an average grain size of 1.5 µm, leading to a maximum electrocaloric temperature change |ΔTEC| of 0.49 K at 40 °C with a broad peak of |ΔTEC| > 0.33 K in the temperature range from 10 °C to 75 °C under an electric field change of 5 V µm-1. By increasing the sintering temperature of BCSSnT-20 from 1350 °C to 1425 °C, the grain size increased from 1.5 µm to 7.3 µm and the maximum electrocaloric temperature change |ΔTEC| increased from 0.15 K at 35 °C to 0.37 K at 20 °C under an electric field change of 2 V µm-1. Our results show that under all investigated material systems, BCSSnT-20 is the most promising candidate for future application in multilayer ceramic (MLC) components for EC cooling devices.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.