Abstract
Gadolinium oxide (Gd2O3) is a potentially effective mineral additive that improves neutron shielding properties of cement based composites. The paper presents the influence of Gd2O3 and ulexite (a boron compound) on Portland cement hydration evaluated by isothermal calorimetry measurements and strength. The progress of hydration was investigated on mortar specimens at water to cement ratio w/c = 0.5 and sand/cement ratio 0.75. The addition of Gd2O3 generates a slight retardation of cement hydration, however it accelerates aluminate activity at the same time. The hydration of cement was completely hindered for mortars containing a substantial content of ulexite. The strength test results show that addition of Gd2O3 to Portland cement mortar mix caused a decrease of early age (3 days) flexural and compressive strength. The optimum content of Gd2O3 in respect to the long term compressive strength and the hydration kinetics was 5% in relation to the mass of cement. Good long term strength was also obtained for specimens with 3% of ulexite.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.