Abstract
nfluence of frequency on fretting fatigue damage behavior of Al-Zn-Mg alloy was studied in this paper. Fretting fatigue lives and damage characteristics of Al-Zn-Mg alloy were researched under different frequencies. Macroscopic tests and microscopic analysis were used to study on influence of frequency on fretting fatigue damage behavior of Al-Zn-Mg alloy. Fatigue lives would be greatly reduced by fretting under the experimental conditions in this paper. With frequency increasing, fretting fatigue lives were firstly decreased and then increased (f=9Hz). Fretting scar, which was the important reason for fretting fatigue crack initiation, was caused by embedding debris; eventually, crack initiated at the edge of the fretting scar. Fretting fatigue fracture is a whole process of crack initiation, propagation and final fracture. And final fracture increased with frequency reducing, which was generally occurred near the center of the fracture.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.