Abstract
The Pd/TiO 2 nanoparticles containing 5 wt.% Pd were synthesized by one-step flame spray pyrolysis (FSP) under different flame conditions. As revealed by both X-ray diffraction (XRD) and transmission electron microscopy (TEM) results, the average particle sizes of Pd/TiO 2 were increased from 9.7 to 24.6 nm with increasing the precursor concentration and the feed flow rate as well as reduction of the O 2 dispersing gas during FSP synthesis. Although the BET surface area and %anatase phase content were decreased with increasing Pd/TiO 2 particle size, %Pd dispersion as determined from the amounts of CO chemisorption were higher on the larger size FSP-made Pd/TiO 2 nanoparticles. It is suggested that the shorter residence time in flame and/or the lower combustion energy (enthalpy density) resulted in more coverage of Pd surface by the formation of Ti–O groups, rendering lower CO chemisorption ability of the smaller size Pd/TiO 2.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.