Abstract
AbstractRubber compounds are filled with reinforcing fillers to improve their physical properties. Carbon black and silica have different surface chemistries to each other. Differences in properties of carbon black‐ and silica‐reinforced styrene‐butadiene rubber (SBR) compounds were studied. Variation of properties of carbon black‐ or silica‐filled compounds with the filler content was also investigated. The silica‐filled compounds without any coupling agent and dispering agent were prepared to investigate the influence of polar materials‐adsorption on the silica surface. Viscosity and crosslink density increased with increase of the filler content. Hardness, modulus, tensile strength, and wear property were improved more and more by increasing the filler content. Viscosity of the silica‐filled compound was higher than that of the carbon black‐filled one. Cure rate of the silica‐filled compound became slower as the filler content increased, while that of the carbon black‐filled one became faster. Difference in properties between the carbon black‐ and silica‐filled compounds were explained by the poor silica dispersion and the adsorption of cure accelerator on the silica surface. Copyright © 2004 John Wiley & Sons, Ltd.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.