Influence of environment, temperature and time of the thermal modification of ash wood (Fraxinus excelsior L.) on the cellulose weight average degree of polymerization . Using the size-exclusion chromatography (HPLC SEC) method, the weight average degree of cellulose polymerization was determined. The polymer was isolated by the Kürschner-Hoffer method from ash wood (Fraxinus excelsior L.). The wood was thermally modified in different environments (nitrogen, steam and air) at 190°C and modification times of 2, 6 and 10 hours. Depending on the anaerobic atmosphere used, the highest values of the weight average degree of cellulose polymerization were obtained for the nitrogen environment, followed by steam and air. The effect of modification time on the weight average degree of polymerization was observed. The highest values were obtained for wood modified at 2 hours, then 6 and 10 hours of modification. The native wood showed the highest degree of polymerization. On the basis of the results obtained, it can be concluded that for the material studied the oxidation and degradation reactions occurring depend on the environment and time for a given temperature of wood modification.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.