Abstract
Bi1.05−xDyxFeO3 (BDFO) (x = 0−0.2) ceramics were synthesized by solid-state reaction method. The influence of Dy dopant on crystal structural, dielectric and ferroelectric properties was investigated. The lattice parameter and the Curie temperature of BDFO were degraded continuously with increasing contents of Dy3+ cations. Leakage current density, ferroelectric polarization and dielectric loss were improved by appropriate Dy doping. When x = 0.1, BDFO showed the best electric properties. At applied electric field of 53 kV/cm, the remnant polarization (2Pr) was 12.2 μC/cm2.These improvements in electric properties in BDFO ceramics could have resulted from the relatively low oxygen vacancy concentration and structural distortion.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: Journal of Materials Science: Materials in Electronics
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.