Abstract
The alginate production by Azotobacter vinelandii, as well as the molecular weight of the polymer, are strongly influenced by the dissolved oxygen tension (DOT) and stirring speed of the culture. Under high DOT (5% of air saturation), the bacteria produced more alginate (4.5 g/l) than that obtained at low (0.5%) oxygen tension (1.0 g/l) in cultures conducted at 300 rpm. On the other hand, under constant DOT (3%), the higher the stirring speed (from 300 to 700 rev./min), the higher the specific growth rate and the alginate production rate. However, low agitation speed (300 rev./min) lead the culture to produce a polymer of high molecular weight (680 000 g/g mol) whereas a low molecular weight (352 000 g/g mol) alginate was isolated from cultures conducted at high (700 rev./min) stirring speed. At 700 rev./min, the MMW increased to a plateau between 1 and 3% DOT and then decreased to a minimum of 0.11 x 10(6) g/g mol at 7%. Microscopic observations revealed the presence of cell aggregates (one order of magnitude larger than individual cells) when the culture was conducted at 300 rev./min. Oxygen gradients occurring within the aggregates could be responsible of this phenomenon. At high agitation rate, the MMW of the alginate dropped towards the end of the culture in all conditions evaluated. Alginase activity was detected, which would be responsible for this phenomenon.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.