Abstract
Introduction:The treatment of dental tissues before adhesive restorative procedures is an important step in the bonding protocol and determines the clinical success of restorations.Aim:The aim of this study is to evaluate in vitro the influence of diode laser on the shear bond strength of one- and two-step self-etch (SE) adhesives to dentin when the laser is applied over the adhesives before photopolymerization.Methodology:About 20 freshly extracted noncarious intact maxillary premolars were collected, and the buccal and lingual surfaces of the tooth were ground with the help of diamond disk under water coolant till dentin was exposed. The specimens were divided into two groups of 10 each. Buccal surfaces of all the specimens were exposed to diode laser before light curing (test/experimental group) act as control group. In Group I, Clearfil SE with laser was used on the buccal surface, whereas in Group II, G-bond SE adhesive with laser was used on the buccal surface. Shear bond test was measured using an universal testing machine and the values were obtained in megapascals (MPa).Results:P < 0.05 was considered statistically significant. According to the results, it was found that the mean bond strength values of the laser-treated groups were significantly higher than groups not treated with laser.Conclusion:Within the limitations of this study, it can be concluded that mean bond strength Clearfil SE with and without laser was significantly higher than G-bond with and without laser values.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.