Abstract
Objective The aim of this study is to verify the influence of three pigment incorporation methods (conventional, mechanical, and industrial) on the sorption and solubility of the MDX4-4210 and A-2186 silicones. Materials and Methods The groups formed were based on the silicones used (A-2186 and MDX4-4210), intrinsic pigments (pink, bronze, and black), and pigment incorporation methods (conventional, mechanical, and industrial). The dimensions of all samples were 45-mm diameter (ø) × 1-mm thickness. Readings were taken initially and after 1,008 hours of aging. Statistical Analysis Three-way analysis of variance and the Tukey's test were performed (α = 0.05). Results For sorption and solubility, there was no difference between the incorporation methods for the A-2186 silicone, regardless of the pigment used ( p > 0.05). For pink MDX4-4210, the industrial and mechanical methods showed higher values of sorption compared with the conventional method ( p < 0.05). For bronze MDX4-4210, the industrial method showed a higher sorption value compared with the conventional and mechanical methods ( p < 0.05). For black MDX4-4210, there was no difference between incorporation methods based on sorption ( p > 0.05). For pink MDX4-4210, the mechanical method showed a higher solubility value compared with the industrial and conventional methods ( p < 0.05). For black MDX4-4210 and bronze MDX4-4210, there was no statistically significant difference between incorporation methods based on solubility (p > 0.05). Conclusion Based on sorption and solubility, for the A-2186 silicone, the conventional, mechanical, and industrial methods of pigment incorporation were equivalent. For the MDX4-4210 silicone, its results of sorption and solubility were varied, and further studies are recommended.
Highlights
Facial defects can be the result of a congenital anomaly, surgical resection of a tumor, and trauma or a combination of these factors.[1]
The aim of this study is to verify the influence of three pigment incorporation methods on the sorption and solubility of the MDX4-4210 and A-2186 silicones
The degradation of the physical and mechanical properties of a silicone prosthesis is related to exposure to ultraviolet rays, air pollution, humidity, improper cleaning, and daily handling.[1,3,4]
Summary
The aim of this study is to verify the influence of three pigment incorporation methods (conventional, mechanical, and industrial) on the sorption and solubility of the MDX4-4210 and A-2186 silicones. Materials and Methods The groups formed were based on the silicones used (A-2186 and MDX4-4210), intrinsic pigments (pink, bronze, and black), and pigment incorporation methods (conventional, mechanical, and industrial). For pink MDX4-4210, the industrial and mechanical methods showed higher values of sorption compared with the conventional method (p < 0.05). For bronze MDX4-4210, the industrial method showed a higher sorption value compared with the conventional and mechanical methods (p < 0.05). For pink MDX4-4210, the mechanical method showed a higher solubility value compared with the industrial and conventional methods (p < 0.05). For black MDX4-4210 and bronze MDX4-4210, there was no statistically significant difference between incorporation methods based on solubility (p > 0.05). Conclusion Based on sorption and solubility, for the A-2186 silicone, the conventional, mechanical, and industrial methods of pigment incorporation were equivalent.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.