Influence of different crosshead speeds on diametral tensile strength of a methacrylate based resin composite: An in-vitro study.

Abstract

Aim:The aim was to evaluate the influence of different crosshead speeds on diametral tensile strength (DTS) of a resin composite material (Tetric N-Ceram).Materials and Methods:The DTS of Tetric N-Ceram was evaluated using four different crosshead speeds 0.5 mm/min (DTS 1), 1 mm/min (DTS 2), 5 mm/min (DTS 3), 10 mm/min (DTS 4). A total of 48 specimens were prepared and divided into four subgroups with 12 specimens in each group. Specimens were made using stainless steel split custom molds of dimensions 6 mm diameter and 3 mm height. The specimens were stored in distilled water at room temperature for 24 h. Universal testing machine was used and DTS values were calculated in MPa.Results:Analysis of variance was used to compare the four groups. Higher mean DTS value was recorded in DTS 2 followed by DTS 4, DTS 1, and DTS 3, respectively. However, the difference in mean tensile strength between the groups was not statistically significant (P > 0.05).Conclusion:The crosshead speed variation between 0.5 and 10 mm/min does not seem to influence the DTS of a resin composite.