Abstract
The paper presents the effect of diamond particle size (varying between 2.5 µm and 20 µm) on the microstructure, density and hardness of WC-Co/diamond composites. The obtained materials contained 30% vol. diamond. The advanced sintering method Pulse Plasma Sintering (PPS) was used for the production of composites. The sintering process was carried out in two stages at a pressure of 50 and 100 MPa and a temperature of 1050 °C. Depending on the size of the diamond particles, composites with a density of 91–99% were obtained. Microstructure studies were performed employing scanning electron microscopy, along with an analysis of the chemical composition in micro-areas. Additionally, the phase composition was investigated by means of X-ray diffraction. In addition, hardness tests were performed. It was found that the size of the diamond particles significantly influenced the microstructure of the tested materials, as well as the density and hardness. As a result of PPS sintering of composites containing the finest diamond particles (2.5–5 µm), the presence of a metastable type of diamond—graphite was found.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.