Abstract
This paper uses several techniques to monitor the ageing of commercial LiFePO4 cells, which are cycled at 55 °C and −20 °C at various depths of discharge. Ageing at lower depth of discharge leads to higher capacity fading, as compared to higher depth of discharge. The highest capacity fading is observed using 50% depth of discharge for cycling at 55 °C, while the lowest capacity fading is observed for the cells aged at 100% depth of discharge when cycled at −20 °C. Using incremental capacity analysis and differential voltage analysis the capacity fading is monitored and underlying ageing mechanisms are described. The loss of lithium inventory and the loss of active material, especially on the cathode side, are the major degradation mechanisms for the cells. The first incremental capacity analysis peak of the discharge process can be used in our case to predict remaining life and cell capacity.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.