Abstract
AbstractCu2+‐Organic montmorillonites were prepared by modifying Na+ montmorillonite (Na+‐MMT) with silane coupling agents and cupric sulfate. PVC/organic montmorillonite composites were prepared by the melt intercalation method. Morphological structure of modified MMT and PVC/MMT was obtained by using XRD and SEM. The XRD results showed that silanes and Cu2+ were intercalated among interlayers and that modified MMT may have exfoliated dispersion in PVC. Effects of Cu2+‐organic montmorillonites on decomposition and smoke emission of poly(vinyl chloride) (PVC) in the flaming mode were investigated by using a cone calorimeter at an incident heat flux of 25 kW·m−2. Cone experimental data demonstrated that the Cu2+‐organic montmorillonites prepared were new effective smoke suppressants. They clearly promoted an early HCl elimination, crosslinking reactions, and char residue formation, based upon the decomposition parameters of mass loss, mass loss rate, and time of initial decomposition (tinitial). Cu2+‐Organic montmorillonites decreased peak heat release rate, total heat release, peak smoke production rate, total smoke production, and smoke extinction area during the flaming process. The smoke‐reducing efficiency of Cu2+‐organic montmorillonites (Cu2+‐OMMTs) was the best. However, the content of cupric ion was only 0.6–0.8% in Cu2+‐OMMTs and 0.03–0.04% in PVC composites. They may make the smoke‐reducing efficiency reach 45–50%. This result further demonstrates that Cu2+ ion is a very effective smoke suppressant for PVC. J. VINYL ADDIT. TECHNOL., 13:31–39, 2007. © 2007 Society of Plastics Engineers.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.