Abstract

Structural and magnetic properties of chemically synthesized magnetite nanoparticles have been studied using X-ray diffraction, Transmission Electron Microscopy and Vibrating Sample Magnetometer. Magnetically the synthesized nanoparticles are ranging from superparamagnetic to multi domain state. Average crystallite size of the synthesized magnetite nanoparticles were determined using X-ray line broadening and are found to be in the range of 9–53 nm. On the other hand, the TEM images show that the size is ranging between 7.9 and 200 nm with the transition from spherical superparamagnetic particles to faceted cubic multi domain particles. Magnetic parameters of the samples show a strong dependence on average crystallite size. The ratio of coercive field at 20 K to that at 300 K (Hc (20 K)/Hc (300 K)) increased sharply with decrease in crystallite size. A critical crystallite diameter of order 36 nm may be inferred as boundary between single domain to multi domain transition. Zero-field-cooled (ZFC) and field-cooled (FC) measurements at 10 Oe field validate the same for smallest and largest size samples, confirming that the anisotropy energy is greater than thermal energy upto 300 K temperature. For 9 nm sample broad ZFC curve with overlapping of FC curve is observed just at 300 K, indicating the effect of strong dipolar field in superparamagnetic system.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.