Abstract
In this paper, we report a detailed study of magnetic properties and AC magnetic heat generation characteristics of La0.77Sr0.23MnO3 (LSMO) nanoparticles to investigate appropriate crystallite size with a view to the proper application of self-controlled magnetic hyperthermia treatments of cancer. A series of nanocrystalline LSMO manganite was synthesized through the chemical route called as “polymerized complex method” and then subsequently annealed at the different temperature from 600 to 1400 °C to obtain various crystallite size. Phase formation and crystal structure of the prepared powder were determined by the powder X-ray diffraction (XRD) using Rietveld analysis. The XRD patterns reveal that all powder samples are a single phase rhombohedral perovskite-like structure with R3¯c space group. The mean crystallite size of prepared particles varied from 19 to 243.8 nm with the increase of the annealing temperature starting from 600 to 1400 °C. The field emission scanning electron microscopy (FE-SEM) analysis shows the surface morphology with a strong agglomeration of fine nanoparticles. The Magnetic study reveals that these nanoparticles exhibit ferromagnetic nature with different value of magnetization, coercivity, Curie temperature which is strongly dependent on their crystallite size. The maximum saturation temperature (TS = 66 °C) under AC magnetic field (H = 1.77 kA/m, f = 370 kHz) was found for the crystallite size of 39.5 nm due to its pure single domain phase. Such LSMO nanoparticles, having the higher heating rate, can be used in magnetically induced hyperthermia cancer treatment.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.