Abstract
Nanostructured tungsten carbide-cobalt coatings were deposited by air plasma spraying (APS) technique, using nitrogen as primary plasma gas. The characteristics of nanostructured coatings are typically affected by the percentage of unmelted/partially-melted regions present in the coatings. Hence, the coatings were obtained as a function of critical plasma spray parameter (CPSP), which is defined as the ratio of arc power to the primary plasma gas flow rate. It was observed that tungsten (W) rather than tungsten carbide (WC) was the dominant phase in nanostructured coatings due to decarburization. CPSP was found to have a significant effect on wear performance of APS nano-structured coatings. Wear resistance was highest for coatings deposited at lowest CPSP. Flaking was more prevalent in nanostructured coatings deposited at the highest CPSP.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.