Abstract
In this work, we present the results of defects analysis concerning ZnO and Al2O3 layers deposited by atomic layer deposition (ALD) technique. The analysis was performed by the X-band electron paramagnetic resonance (EPR) spectroscopy, transmission electron microscopy (TEM) and X-ray photoelectron spectroscopy (XPS) methods. The layers were either tested as-deposited or after 30 min heating at 300 °C and 450 °C in Ar atmosphere. TEM and XPS investigations revealed amorphous nature and non-stoichiometry of aluminum oxide even after additional high-temperature treatment. EPR confirmed high number of defect states in Al2O3. For ZnO, we found the as-deposited layer shows ultrafine grains that start to grow when high temperature is applied and that their crystallinity is also improved, resulting in good agreement with XPS results which indicated lower number of defects on the layer surface.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.