Abstract
The influence of cold work (CW) on electrochemical behavior of 316L ASS in PEMFC (0.5M H2SO4 + 2 ppm HF at 70 °C) environment was investigated by microstructural observations, x-ray diffraction (XRD), polarization, electrochemical impedance spectroscopy (EIS) and Mott-Schottky (M-S) techniques. The XRD is used to analyze the increase in dislocation density and formation of α′-martensite with increasing CW degree. The EIS is used to find out the effect of substrate dislocation density on the film resistance. The EIS result show that with increasing CW, the diameter of depressed semi-circular arc and consequently film resistance decreased. This indicates the formation of highly disordered and porous film on CW. From PDP results, it is found that icrit, ip and icorr increased on increasing CW degree. Moreover, the direct relationship was drawn from the dislocation density of the substrate to the defect density of the passive film from M-S technique.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.