Abstract
The research was carried out on 26Mn-3Si-3Al steel having a low value of SFE. After casting, steel was forged and hot-rolled at the temperatures within the range of from 1200°C to 900. Next, the steel was cold rolled until the deformation of 66% was obtained. Upon the basis of X-ray examination and the observations of microstructures, it was found out that during cold rolling mechanical twinning and the martensitic transformation of austenite in hcp-ε martensite occurred. The crystallographic texture of the γ phase (austenite) and ε phase (martensite) was also examined.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.