Influence of Chloride Ion Concentration on Corrosion Behavior of WC–MgO Composite

Abstract

The influence of chloride ion (Cl−) concentration on the corrosion mechanism of WC–MgO composites has been studied in this work. The results suggest that the corrosion resistance of WC–MgO composite decreases first and then increases with the increase in Cl− concentration. Solution conductivity and dissolved oxygen content are the main influence factors. The solution conductivity determines the charge transfer process, and the dissolved oxygen determines the cathodic oxygen absorption reaction. The corrosion characteristic is typical pitting corrosion. Meanwhile, the corrosion mechanism contains an oxidation process of the WC matrix and the dissolution destruction of the MgO toughening phase. The formation of the WO3 corrosion layer hinders the general corrosion to protect the inner material. However, the dissolution of MgO induces the initiation of pitting. The local alkaline caused by MgO dissolution promotes the dissolution of the WC matrix, which leads to the expansion of pitting.