Abstract
The kinetics of the glass transition and the characteristic size of the fluctuating spatio-temporal domains in supercooled glass-forming liquids, i.e., the Cooperatively Rearranging Regions (CRR), were measured upon cooling over a broad range of cooling rates using Differential Scanning Calorimetry (DSC) and chip-based Fast Scanning Calorimetry (FSC). The investigations were conducted on a selection of fragile glass formers (fragility indices between 80 and 140), with a large variance in the atomic or molecular structure but comparable thermal glass transition temperatures Tg, with the aim of evaluating the influence of chemical composition and structure on the CRR size and the associated temperature fluctuation. The selected materials are two polymers (poly(vinyl acetate) (PVAc), poly(lactic acid) (PLA)) as well as the simplest chalcogenide glass-former (selenium). It turned out that the CRR size plotted against the reduced temperature T/Tg follows the same trend, irrespective of the considered glass-former.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.