Abstract
The influence of the casting filling technique and hot isostatic pressing (hipping) on the fatigue-life distribution of Al-7Si-Mg alloy castings has been studied. To vary the number density and size of oxide-film defects in the castings, test bars were cast using bottom-gated filling systems with and without filtration. Some unfiltered castings were subjected to a hipping treatment of 100 MPa at 500 °C for 6 hours. Test pieces were machined from the castings and were fatigue tested in pull-pull sinusoidal loading, at maximum stresses of 150 and 240 MPa under a stress ratio of R=+0.1. The fatigue lives at any probability of failure and Weibull statistical parameters of the filtered castings were higher than those of the unfiltered and nonhipped castings, illustrating the importance of the casting technique. However, the unfiltered but hipped castings exhibited higher performance. It is proposed that the significant improvement in fatigue life after hipping is due to the deactivation of entrained double oxide-film defects as fatigue-crack initiators.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.