Abstract
Tension-tension fatigue tests were performed to examine the influence of carbon content on the fatigue properties of drawn specific steel tube (STB340) with/without post heat treatment for small once-through boiler. Two different carbon content steel tubes, C =0.06 and 0.12% were prepared. The as-received, as-drawn and post drawing heat treated series for each carbon content tube were prepared for fatigue test. The hardness, grain size and residual stress were measured for each series. As a result, the fatigue strength of as-received and as-drawn series showed a small difference between C =0.06 and 0.12% specimens. However, the post drawing heat treatment series showed obvious difference in the fatigue strength. The fatigue strength of higher carbon content tubes significantly decreased by the post drawing heat treatment, whereas the decrease of fatigue strength was little for lower carbon content heat treated tubes. The difference of fatigue strength was mainly caused by the degree of relaxation of work hardening by post heat treatment.
Sign-in/Register to access full text options 
Free) 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call